Structural, magnetic, and gigahertz-range electromagnetic wave absorption properties of bulk Ni–Zn ferrite | Scientific Reports

Oct 14, 2024

Scientific Reports volume 11, Article number: 9468 (2021) Cite this article

5096 Accesses

39 Citations

1 Altmetric

Metrics details

Nickel–zinc ferrite (Ni0.5Zn0.5Fe2O4) powders were prepared by the conventional solid-state route and sintered at 1100 and 1300 °C for utilization as a tile electromagnetic wave absorber. Structural, magnetic, and microwave absorption properties were investigated by characterization techniques of X-ray diffraction, thermogravimetric analysis, Raman spectroscopy, electron microscopy, vibrating sample magnetometry, and vector network analyzer. The samples sintered at 1300 °C showed high magnetic saturation of 87 emu/g and low coercivity of 4 Oe. Electromagnetic investigations exhibit high reflection losses up to − 48.1 dB at certain high and low gigahertz frequencies, as clearly depicted in the 3D contour plot. The optimized condition between reflection loss, thickness, and bandwidth revealed a reflection loss of about − 36.1 dB at the matching thickness of 3.7 mm for the X-band. Furthermore, the effective working bandwidth at − 10 dB was up to ~ 7.1 GHz for the minimum thickness of 4.3 mm, which thoroughly covered the C-band. The microwave absorption performance of the well-sintered Ni–Zn ferrite was attributed to the incorporation of dielectric and magnetic loss mechanisms in which the magnetic part prevails.

Wireless communication transmitting information from one point to another, without using any connection like wires, cables, or any physical medium, is widely used in mobile phones, GPS receivers, remote controls, and Wi-Fi, owing to its inexpensive, mobility, easiness, and reliability1,2. However, there are few drawbacks such as interference, security, and probable health issues for wireless communications3,4,5. The interference of electromagnetic (EM) waves from various devices can be led to high amounts of noise in connections by undesired constructive/destructive ways6,7,8,9. Among various methods, the shielding of electronic devices by microwave absorbers is an attractive and practical method to be safe against electromagnetic interferences and brings good electromagnetic compatibility (EMC) for the operating devices10,11. An ideal absorber material for electromagnetic interference (EMI) shielding should have high dielectric and magnetic losses, chemical stability, low-cost, and lightweight12,13.

Dielectric14, magnetic15, and carbon-based16,17 materials could be utilized as EM wave absorbers in order to attenuate the distinct frequency range and reducing the interference caused by airborne connections18. In addition to the attenuation ability, which is related to dielectric and magnetic losses, another challenging issue is that an absorber material should fulfill the impedance matching condition \(\left( {z = \sqrt {{\raise0.7ex\hbox{$\mu $} \!\mathord{\left/ {\vphantom {\mu \varepsilon }}\right.\kern-\nulldelimiterspace} \!\lower0.7ex\hbox{$\varepsilon $}}} \sim1} \right)\) to receive incident EM waves with the lowest reflectivity. In most cases, absorber materials possess low permeability and high permittivity, while magnetic spinel ferrites have the competency of good impedance matching according to their higher permeability over other absorbers. Spinel ferrites (MFe2O4, M = Co, Ni, Mn, Zn, Fe, Cu) as soft magnetic materials can be used for diverse applications such as home and industrial electronic devices19,20, biomedicals21,22,23, catalysts24,25, and further in EMI shielding as absorber materials because of their relatively high dielectric/magnetic loss, excellent chemical stability, and low costs26,27. Nickel–Zinc ferrite shows better EM wave absorption performances compared to other spinel ferrites due to higher resistivity, high saturation magnetization, and high permeability28,29,30. The spinel Ni–Zn ferrite has a cubic crystal structure with the space group of Fd3m in which the cations are distributed between tetrahedral (A) and octahedral [B] sites12. The occupation of (A) sites and [B] sites strongly depends on the ionic radius, crystal field, electron configuration, and ionic polarization of cations31,32. Accordingly, the Zn2+ cations are usually preferred to occupy (A) sites because of crystal energy stabilization, while the octahedral [B] sites are appropriate for Ni2+ cations33,34. The Fe3+ cations can distribute between (A) sites and [B] sites due to the low crystal field energy stabilization35. The higher saturation magnetization (Ms) of Ni0.5Zn0.5Fe2O4 ferrites than that of NiFe2O4 ferrite is due to the higher difference of magnetic moments between (A) sites and [B] sites, which is induced by Zn2+ doping36,37.

Up now, alongside the reports on the electromagnetic properties of Ni–Zn ferrite in the low frequency ranges38,39,40, Huang et al.35 studied the magnetic and microwave absorption properties of paraffin/Ni–Zn nanofiber and expressed a magnetic saturation of about 77 emu/g and a reflection loss (RL) of − 14.1 dB at 10.9 GHz. Aggarwal and Narang41 investigated the 8.2–12.4 GHz range electromagnetic properties of the nickel–zinc ferrite prepared by the sol–gel route and reached to minimum reflection loss of − 17.5 dB with the effective absorption band length of 3.1 GHz. Mustaffa et al.42 scrutinized the microwave absorption properties of MWCNT/Ni–Zn composite and gained an RL = − 19.3 dB with the bandwidth of 1.24 GHz at X band frequency.

In microwave absorber application, spinel ferrite powders were usually prepared by a solid-state43,44 or a wet chemical route45,46 and mixed with different amounts of a suitable non-conductive or conductive polymer as the dispersant medium, and the composite mixture can be applied as coating47,48. The polymer/ferrite composites are disposed to destruct in harsh environments and do not have good durability as a permanent coating49. Moreover, it was mostly reported that the EM wave absorption performance might improve by maximizing the Ni–Zn ferrite content50,51, but the limitations of adding high amounts of ferrite powders besides the lack of integrity of the polymer-based coatings49, lead our team to investigate the microwave absorption properties of sintered Ni–Zn ferrite in a wide 1–18 GHz frequency range for utilization as tile absorber. Also, Naidu52 showed that bulk Ni–Mg ferrite has better microwave absorption properties than that of Ni–Mg nanoferrites. In the present work, bulk Ni0.5Zn0.5Fe2O4 samples were fabricated by the conventional ceramic method, and the structural, microstructural, magnetic, and microwave absorption properties were studied as a function of sintering temperature.

The Ni–Zn ferrite powders were synthesized by the conventional solid-state method. Analytical grade of Fe2O3, ZnO, and NiO powders in stoichiometric amounts (1:0.5:0.5) was mixed by using a planetary ball mill (Sanat Ceram, Iran) in a wet ethanol medium. The milling rotational speed was set at 200 rpm for 7 h with the ball to powder ratio (BPR) of 20. The obtained mixture was dried in the oven at 70 °C and then calcined at 900 °C in the air atmosphere. The calcined powders were ground again to break the large agglomerates. The as-calcined NiZn ferrite powders were uniaxially pressed into both disk-shaped (d = 10 mm) and toroidal ones (din = 3 mm and dout = 7 mm) under the pressure of 250 MPa. The compacted bodies were sintered at 1100 and 1300 °C for 2 h in the air atmosphere. The schematic of the synthesis procedure is shown in Fig. 1.

Schematic of the samples synthesis route.

Thermogravimetric analysis was operated with a simultaneous thermal analyzer (BAHR 504) from room temperature up to 1500 °C with the same condition used for calcination and sintering to show the thermal stability of the samples. The structural properties were characterized using an Ultima IV X-ray diffractometer (Rigaku, Japan) with Cu Kα (λ = 1.5406 A) radiation. Crystal structure analysis of the XRD patterns was done using Highscore plus software, and the lattice parameter and cation distribution of the samples were calculated by the Rietveld refinement method. The nickel–zinc ferrite belongs to the spinel Fd3m space group; therefore, oxygen positions (x = y = z) were taken as free parameters, while other atomic fractional positions were held as fixed. Moreover, lattice constants, isothermal parameters, occupancies, scale factors, and shape parameters were also taken as free parameters. Refinement steps were continued until the goodness of fit (\(\sigma^{2}\)) reaches to the values close to 1.5, showing the convergence of the refined profile with the observed patterns and confirming the quality of fit53. Cation distribution was obtained by taking into account the presence of both inverse and normal spinel structures. The nickel ferrite was modeled as complete inverse, while the zinc ferrite was considered as complete normal spinel. Furthermore, Raman spectroscopy was done using an XploRA PLUS (HORIBA, Japan) with a 785 nm laser line operated at room temperature. The microstructural characteristics were observed by a Mira 3 field-emission scanning electron microscope (TESCAN). An energy-dispersive detector with an accelerating voltage of 15 kV was used to depict the elemental composition. A vibrating sample magnetometer (Meghnatis Daghigh Kavir Co., Iran) was used to measure the magnetic properties at room temperature. The applied field was swept from − 10 to10 kOe. Electromagnetic properties, including permittivity and permeability spectra, were obtained using an 8722 ES network analyzer (Agilent/HP) in the wide frequency range of 1–18 GHz.

Figure 2 represents the DTA-TG plot of as-prepared powders. The initial mass reduction (about 5%) starts from ambient temperature up to 600 °C due to the elimination of physically absorbed water in most (3.5% up to 250 °C) and dehydroxylation and decomposition of residual organic compounds. Three critical temperatures in TG curve at 900, 1100, and 1300 °C were chosen for further thermal treatments of calcination and sintering where the main mass reduction occurs, spinel phase formation initiates, and sintering phase completes, respectively. Moreover, fluctuations of DTA curve at about 930, 1120, and 1280 °C were attributed to the mentioned critical temperatures, where the broad endothermic peak at 1200–1400 °C can also be assigned to the grain growth step of the sintering. Small fluctuations and negligible mass changes in the thermally analyzed sample illustrate the stability of the compound at higher temperatures54.

DTA/TG analysis results of the as-milled powders.

Figure 3 shows the XRD patterns of the initial mixture, as-calcined Ni–Zn ferrite powder, and sintered samples. During the calcination process, the finely crushed NiO, ZnO, and Fe2O3 powders disappear by reacting the ZnO species with Fe2O3 to crystallize the zinc ferrite (ZnO.Fe2O3). After that, the NiO species slowly diffuses into zinc ferrite to produce NiZn ferrite (Ni0.5Zn0.5Fe2O4) powders55,56. Therefore, the chemical reaction with stoichiometric ratios can be written as \(0.5{\text{NiO}} + 0.5{\text{ZnO}} + {\text{Fe}}_{2} {\text{O}}_{3} \to {\text{Ni}}_{0.5} {\text{Zn}}_{0.5} {\text{Fe}}_{2} {\text{O}}_{4}\). The diffraction peaks of the as-calcined powders and sintered samples at 2θ = 30.04°, 35.40°, 37.03°, and 43.03° are related to (022), (311), (222), (004) planes of the spinel structure of N0.5Zn0.5Fe2O4 phase (PDF2# 00-052-0278), respectively. Although a small peak of Fe2O3 phase was detected in the XRD pattern of calcined sample at ~ 33°, the absence of any other peaks at higher temperatures confirms the purity of sintered Ni–Zn ferrite samples. The lattice constant, density, cations distribution, dislocation density, and strain of the samples versus sintering temperature are shown in Table 157. The lattice constant (a) decreases from 8.3892 to 8.3872 Å, while the density increases from 4.31 to 4.92 g cm−3 because of the reduction of crystal defects with the increase of sintering temperature. Distribution of cations show that the Zn cations are preferred to occupy tetrahedral (A) sites, while the Ni and Fe cations are distributed between tetrahedral (A) and octahedral [B] sites in which the fraction of Fe cations in (A) site as inversion coefficient decreases from 0.4 to 0.3 with the sintering temperature.

XRD patterns of the as-milled and calcined powders at 900 °C and the samples sintered at 1100 and 1300 °C (▽: ZnO, ◆: NiO, and ◄: Fe2O3).

Figure 4 shows the Raman spectra of the sintered samples at 1100 and 1300 °C. Small and broad peaks at about 210, 300, 460, 640, and 680 cm−1 are related to the five active Raman modes of T2g(1), Eg, T2g(2), T2g (3), and A1g58. Low Raman shifts revealed the presence of octahedral B-sties (BO6), while the observed peaks at about 640–700 cm−1 are attributed to oxygen motion in the tetrahedral A-sites (AO4) having A1g mode Raman character59,60. This broad containing shoulder peak was also been assigned to the order–disorder effect of ions over A and B sites61. The related active Raman shifts presented in Table 2 confirms the formation of cubic spinel ferrite, Fd3m, in the sintered samples. Also, all Raman peaks blue shifted slightly toward higher wavenumber due to the increase in sintering temperature (to 1300 °C), where the crystal defects and strain reduced and consequent lower lattice parameter values were obtained30.

Raman spectra of the sintered samples.

FESEM micrographs and EDS analysis of the sintered samples at 1100 and 1300 °C are presented in Fig. 5. The samples sintered at 1100 °C have small (~ 0.3 µm) and discrete grains, while the large grains (~ 10 µm) with smooth grain boundaries appear for sintering at 1300 °C. This may affect the magnetic and microwave absorption properties of the samples through the interface effects62,63. Also, it can be observed that the Ni–Zn ferrite particles cannot be grown and sintered at the lower temperature. Densification is chiefly related to grain boundary (GB) diffusion, while grain growth is ruled by GB migration. The abnormal grain growth at 1300 °C can be attributed to the small grain size of Ni–Zn ferrite powders, providing a large amount of activation energy for grain boundary migration. Some small pores are also trapped inside the ferrite grains because of the diffusion lag during the sintering process. Although some pores may be trapped, the resultant structure has lower defects and pores and therefore possess more strength comparing with non-sintered structure. Moreover, with the increase of sintering temperature from 1100 to 1300 °C, the density of samples increases from 4.31 to 4.92 g cm−3, respectively, which are 80.5 and % 91.9 of theoretical density (ρXRD), confirming the decrease of pores and increase of the strength during sintering. Reddy et al.64 reported that the 0.5 atomic Zn ion enhanced the sintering and led to higher grain growth. Also, Mangalaraja et al.65 obtained the highest mechanical properties for the samples with Zn = Ni = 0.5 sintered at 1350 °C. The EDAX analysis shows the various elements are uniformly distributed in the grains and grain boundaries.

SEM micrographs and EDS maps of the samples sintered at (a, b) 1100 and (b, c) 1300 °C.

Figure 6 compares the magnetization curve of the sintered samples. The samples sintered at 1100 °C have the saturation magnetization (Ms) of 56 emu/g with the coercivity (Hc) of 12 Oe, which the coercivity decreases to 4 Oe and the Ms increases to 87 emu/g for 1300 °C. The reduction of Hc can be attributed to the large grains, facilitating the magnetic domain wall motion. Also, the smooth interfaces here may decrease the Hc, according to the reports on the effect of interface roughness on increasing the Hc63,66. Aggarwal and Narang67 gained the highest Ms of about 71 emu/g and Hc of 35 Oe for the samples prepared by sol–gel followed by 8 h of heat treatment at 1000 °C. The same magnetization of 72 emu/g with a very low coercivity of 2 Oe was attained by Liu et al.68 at a higher sintering temperature of 1250 °C. The magnetization of spinel ferrites is mainly dependent on purity, crystallinity, and cations distribution between tetrahedral and octahedral sites46,69. In the collinear two sublattice model, the magnetic moments in the tetrahedral (MA) and octahedral (MB) sites mostly determined the final magnetization value of the samples rather than the A–A and B–B exchange interactions. The most |MA − MB| absolute difference value leads to the highest Ms value of the ferrite samples. Zn as a non-magnetic ion could modify the amount of magnetization in the ferrite sample by inducing the magnetic cation migration from tetrahedral to octahedral sites. According to Neel’s theory, the high imbalance of magnetic ions such as Fe3+ and Ni2+ between (A) and [B] sites (Table 1) results in the high saturation magnetization for the sample sintered at 1300 °C. The higher imbalance of Fe3+ cations for higher sintering temperatures can be attributed to the higher cooling rate70 and crystal strains. Moreover, the high crystallinity and large grains are also beneficial for the increase of Ms at higher sintering temperatures.

Magnetic hysteresis curves of the samples sintered at 1100 and 1300 °C.

Figure 7 shows the permittivity (εr = ε′ − jε″) and permeability (µr = µ′ − jµ″) spectra of the sintered sample at 1300 °C. The real parts of spectra are related to the storage of electrical and magnetic energy, while the energy dissipation is shown by imaginary parts. The values of ε′ decrease versus frequency from 6 at 1 GHz to 5.7 at 18 GHz with an average value of about 5.8. The values of ε″ show two characteristic peaks at ~ 8.5 and 14.5 GHz over the 1–18 GHz range. The electrical energy of EM waves is dissipated by the conductivity and polarization mechanisms. The atomic, electronic, and dipolar polarizations are the main mechanisms of dielectric loss71. Among them, only dipolar polarizations occur in the microwave range due to the interfacial relaxations in which the accumulation of free charges at grain boundaries and defects of material enhances the dipoles72,73,74. The complex permittivity (εr) can be effectively modeled by considering the Debye equation for dipolar polarization and \(\frac{\sigma }{{\omega \varepsilon_{0} }}\) for conductivity losses as follows75:

where the first term describes the superposition of different relaxation mechanisms and the second one is related to the contribution of electrical conductivity \(\left( {\frac{\sigma }{{\omega \varepsilon_{0} }}} \right)\) in which σ = σdc + σac. The ω = 2πf is the operating angular frequency, the values of εr0i and εr∞i are permittivity at low‐frequency and high‐frequency, respectively, τi is the relaxation time, and 0 < αi < 1 is a non‐ideality empirical constant in ith relaxation mechanism. Large ferrite grains are partially conductive, whereas grain boundaries have poor conductivity. At high-frequency ranges, large grains prevail grain boundaries which were effective at low frequencies. Also, the Maxwell–Wagner double layer model expressed that ε′ is decreased and σac is increased as frequency increased76. Therefore, the dispersive behavior of ε″ values with the frequency can be attributed to the higher contribution of AC conductivity (σac). Furthermore, the peaks of ε″ spectra are related to the contributed relaxations, such as interfacial polarization between the ferrite grains, as can be confirmed by the Cole–Cole plot (Fig. 8a)77,78.

Permittivity and permeability spectra of the sample sintered at 1300 °C.

(a) Cole–Cole plot and (b) frequency dependence of μ″ (μ′)−2f−1 of the sample sintered at 1300 °C.

Figure 7c and d show the real and imaginary parts of permeability versus frequency. The values of μ′ and μ″ decrease with the increase of frequency because of the magnetization relaxations79,80. The magnetic losses in the GHz region are mainly related to the eddy current and ferromagnetic resonance mechanisms81,82. The ferromagnetic resonances, including the natural resonance and wall resonance, occur in the MHz range for the soft magnetic NiZn spinel ferrite due to its low anisotropy field (HA)83,84. However, the natural resonance was observed at higher frequencies (GHz range) because of the exchange resonance29,85,86. On the other hand, the eddy current effect loss can be the main mechanism in the GHz region for spinel ferrites. The eddy current loss is dominant when the value of C0 = 2πt2σμ0 = μ″ (μ′)−2f−1 is independent of frequency87. As shown in Fig. 8b, the C0 values are constant at above 12 GHz, indicating the predominance of the eddy current loss.

The permittivity (εr) and permeability (μr) parameters can be used for the calculation of normalized impedance of absorber (Zin) relative to free space (Z0) and reflection loss RL (dB) versus frequency (f) and thickness (t), according to the transmission line theory as follows88,89:

The dependency of reflection loss on the frequency and thickness is shown as a 3D contour plot in Fig. 9a. The higher magnetic and dielectric loss of EM waves by the absorber leads to a more negative RL because of the lower wave reflection from the absorber. High reflection loss up to − 48.1 dB is attained at the frequency range of 1–18 GHz, as shown in the 3D plot. Also, by data extraction from the plot, well-known Wireless LAN protocols of IEEE 802.11b, y, and j at ~ 2.4, 3.65, and 5 GHz can be fully suppressed by the NiZn ferrite absorber. Furthermore, the optimum matching thickness at each frequency band was determined for obtaining the maximum RL and wide effective bandwidth (bandwidth at − 10 dB), as shown in Fig. 9b. The sintered Ni–Zn ferrite showed the maximum RL of − 36.1 dB at the matching frequency of 10 GHz (X-band) in the matching thickness of 3.7 mm, having twice lesser reflection loss than that of Aggarwal and Narang41 reported at the same frequency band (− 17.54 dB at 9.62 GHz) and close to the Nd-doped nickel–zinc ferrite fabricated by Jiao et al.90 (− 37 dB at 8.4 GHz). For evaluating the current study microwave absorption performance with that of other researchers, Table 3 gives a comparison by representing the composition, fabrication method, minimum reflection loss (RLmin), matching frequency (fm), effecting working bandwidth (EWB), and matching thickness (tm) of the similar Ni–Zn ferrite studies in the gigahertz region. The predominancy index (PI) as the ratio of effective bandwidth to matching thickness at various bands is shown in Fig. 10a91. The values of PI are 0.29, 0.56, 0.79, 0.44, and 0 for S, C1, C2, X, and Ku bands. The maximum effective bandwidth at the minimum matching thickness is for the C2 band. Mustaffa et al.42 reported the microwave absorption properties of MWCNT/Ni0.5Zn0.5Fe2O4 composite in the X-band and obtained the PI index of about 0.11 at the matching thickness of 3 mm. The energy of EM waves is consumed by both dielectric and magnetic losses, can be compared by loss factor (tanδ) versus frequency (Fig. 10b). It defines as the ratio of imaginary to real components of the complex permittivity and permeability spectra. The magnetic loss is dominant in the range of 1–12 GHz, while the dielectric loss at above 12 GHz. The magnetic loss can be attributed to the resonance mechanisms at the frequency of 1–12 GHz and the eddy current loss at 12–18 GHz.

(a) Reflection loss (RL) plots showing the distribution of RL versus thickness and frequency and (b) RL plots for the optimum thickness in various bands.

(a) PI index for various bands and (b) dielectric and magnetic loss versus frequency.

The total contribution of dielectric and magnetic attenuation ability can be evaluated by the attenuation constant (α), which is defined by the following equation97:

Figure 11a shows a broad peak in the frequency range of 2–12 GHz in which the increase of α values is related to the high contribution of dielectric and magnetic losses, while the strong reduction of dielectric loss results in the decrease of α values at higher frequencies. The incident EM waves can penetrate the absorber with the minimum reflection when the input impedance is well-matched with free space (Z0). In other words, the modulus of normalized impedance, \(\left| Z \right| = \left| {\frac{{Z_{in} }}{{Z_{0} }}} \right|\), should be approached to 198,99. Figure 11b presents the normalized impedance at different matching thicknesses. It can be found that the values of |Z| are enough close to 1 at higher thicknesses. Therefore, the EM waves can be easily penetrated to the absorber and attenuated by magnetic and dielectric loss mechanisms.

(a) Attenuation values versus frequency, and (b) normalized impedance versus frequency and thicknesses.

Due to the emergence of wireless communications, the utilization of electromagnetic absorber materials is mandatory to reduce electromagnetic interference and bring electromagnetic compatibility for electronic devices. In this research, Ni–Zn ferrite (Ni0.5Zn0.5Fe2O4) bulk samples were fabricated to use as a tile microwave absorber material in the wide 1–18 GHz frequency range. The sample sintered at 1300 °C had a large grain size (~ 10 µm) with smooth grain boundaries. In addition, higher sintering temperature led to appropriate magnetic properties, including high saturation magnetization of 87 emu/g and low coercivity of 4 Oe. 3D reflection loss plot showed the distribution of loss over the 1–18 GHz frequency range in which high reflection losses up to − 48.1 dB were obtained at certain low and high frequencies. The optimized condition by the preference of working bandwidth was in the range of ~ 3 to 10.1 (7.1) GHz for the sample with the matching thickness of 4.3 mm with RL of − 16.9 dB, while by RL preference, the minimum value of − 36.1 dB was achieved at the thickness of 3.7 mm with the effective absorption bandwidth of 6.7 (4.7–11.4) GHz. The absorption performance of the sintered Ni–Zn ferrite was related to easy penetration of EM waves and further attenuation by magnetic and dielectric loss mechanisms. The magnetic loss was attributed to the resonance mechanism, while the interfacial polarization was responsible for the dielectric loss.

Cao, M.-S. et al. Electronic structure and electromagnetic properties for 2D electromagnetic functional materials in gigahertz frequency. Ann. Phys. 531, 1800390. https://doi.org/10.1002/andp.201800390 (2019).

Article CAS Google Scholar

Lv, H. et al. A flexible microwave shield with tunable frequency-transmission and electromagnetic compatibility. Adv. Funct. Mater. 29, 1900163. https://doi.org/10.1002/adfm.201900163 (2019).

Article CAS Google Scholar

Ozdemir, F. & Kargi, A. In Electromagnetic Waves Ch. 22 (ed Vitaliy, Z.) 473–492. https://doi.org/10.5772/16343 (IntechOpen, 2011).

Goldman, A. In Modern Ferrite Technology 273–290. https://doi.org/10.1007/978-0-387-29413-1_11 (Springer, 2006).

Deniz, O. G. et al. Effects of short and long term electromagnetic fields exposure on the human hippocampus. J. Microsc. Ultrastruct. 5, 191–197. https://doi.org/10.1016/j.jmau.2017.07.001 (2017).

Article PubMed PubMed Central Google Scholar

Hwang, Y. Microwave absorbing properties of NiZn-ferrite synthesized from waste iron oxide catalyst. Mater. Lett. 60, 3277–3280. https://doi.org/10.1016/j.matlet.2006.03.010 (2006).

Article CAS Google Scholar

Kotsuka, Y. In Electromagnetic Wave Absorbers 1–15. https://doi.org/10.1002/9781119564430.ch1 (2019).

Tugirumubano, A., Vijay, S. J., Go, S. H., Kwac, L. K. & Kim, H. G. Characterization of electromagnetic interference shielding composed of carbon fibers reinforced plastics and metal wire mesh based composites. J. Mark. Res. 8, 167–172. https://doi.org/10.1016/j.jmrt.2017.08.013 (2019).

Article CAS Google Scholar

Jagadeesh Chandra, R. B., Shivamurthy, B., Kulkarni, S. D. & Kumar, M. S. Hybrid polymer composites for EMI shielding application—a review. Mater. Res. Express 6, 082008. https://doi.org/10.1088/2053-1591/aaff00 (2019).

Article ADS CAS Google Scholar

Zhang, Y. et al. Synthesis of broad microwave absorption bandwidth Zr4+–Ni2+ ions gradient-substituted barium ferrite. Ceram. Int. 46, 25808–25816. https://doi.org/10.1016/j.ceramint.2020.07.062 (2020).

Article CAS Google Scholar

Ibrahim, I. R. et al. A study on microwave absorption properties of carbon black and Ni0.6Zn0.4Fe2O4 nanocomposites by tuning the matching-absorbing layer structures. Sci. Rep. 10, 3135. https://doi.org/10.1038/s41598-020-60107-1 (2020).

Article ADS CAS PubMed PubMed Central Google Scholar

Harris, V. G. Modern microwave ferrites. IEEE Trans. Magn. 48, 1075–1104. https://doi.org/10.1109/TMAG.2011.2180732 (2012).

Article ADS CAS Google Scholar

Idris, F. M. et al. Recent developments of smart electromagnetic absorbers based polymer-composites at gigahertz frequencies. J. Magn. Magn. Mater. 405, 197–208. https://doi.org/10.1016/j.jmmm.2015.12.070 (2016).

Article ADS CAS Google Scholar

Green, M. et al. Doped, conductive SiO2 nanoparticles for large microwave absorption. Light Sci. Appl. 7, 87. https://doi.org/10.1038/s41377-018-0088-8 (2018).

Article ADS CAS PubMed PubMed Central Google Scholar

Chang, Y. et al. Microwave absorption in 0.1–18 GHz, magnetic and structural properties of SrFe12−xRuxO19 and BaFe12−xRuxO19. J. Alloys Compd. 818, 152930. https://doi.org/10.1016/j.jallcom.2019.152930 (2020).

Article CAS Google Scholar

Wu, Z. et al. Hierarchically porous carbons derived from biomasses with excellent microwave absorption performance. ACS Appl. Mater. Interfaces 10, 11108–11115. https://doi.org/10.1021/acsami.7b17264 (2018).

Article CAS PubMed Google Scholar

Bhattacharyya, R. et al. Graphene oxide-ferrite hybrid framework as enhanced broadband absorption in gigahertz frequencies. Sci. Rep. 9, 12111. https://doi.org/10.1038/s41598-019-48487-5 (2019).

Article ADS CAS PubMed PubMed Central Google Scholar

Sebastian, M. T., Ubic, R. & Jantunen, H. Microwave Materials and Applications Vol. 2 (Wiley, 2017).

Book Google Scholar

Krishnaveni, T., Kanth, B. R., Raju, V. S. R. & Murthy, S. R. Fabrication of multilayer chip inductors using Ni–Cu–Zn ferrites. J. Alloys Compd. 414, 282–286. https://doi.org/10.1016/j.jallcom.2005.07.029 (2006).

Article CAS Google Scholar

Dalawai, S. P., Shinde, T. J., Gadkari, A. B. & Vasambekar, P. N. Ni–Zn ferrite thick film gas sensors. J. Mater. Sci. Mater. Electron. 26, 9016–9025. https://doi.org/10.1007/s10854-015-3585-z (2015).

Article CAS Google Scholar

Kharat, P. B., Somvanshi, S. B., Khirade, P. P. & Jadhav, K. M. Induction heating analysis of surface-functionalized nanoscale CoFe2O4 for magnetic fluid hyperthermia toward noninvasive cancer treatment. ACS Omega 5, 23378–23384. https://doi.org/10.1021/acsomega.0c03332 (2020).

Article CAS PubMed PubMed Central Google Scholar

Patade, S. R., Andhare, D. D., Somvanshi, S. B., Kharat, P. B. & Jadhav, K. M. Effect of zinc doping on water-based manganese ferrite nanofluids for magnetic hyperthermia application. AIP Conf. Proc. 2265, 030557. https://doi.org/10.1063/5.0017051 (2020).

Article Google Scholar

Somvanshi, S. B., Kumar, R. V., Kounsalye, J. S., Saraf, T. S. & Jadhav, K. M. Investigations of structural, magnetic and induction heating properties of surface functionalized zinc ferrite nanoparticles for hyperthermia applications. AIP Conf. Proc. 2115, 030522. https://doi.org/10.1063/1.5113361 (2019).

Article CAS Google Scholar

Jadhav, S. A., Somvanshi, S. B., Khedkar, M. V., Patade, S. R. & Jadhav, K. M. Magneto-structural and photocatalytic behavior of mixed Ni–Zn nano-spinel ferrites: visible light-enabled active photodegradation of rhodamine B. J. Mater. Sci. Mater. Electron. 31, 11352–11365. https://doi.org/10.1007/s10854-020-03684-1 (2020).

Article CAS Google Scholar

Borade, R. M., Somvanshi, S. B., Kale, S. B., Pawar, R. P. & Jadhav, K. M. Spinel zinc ferrite nanoparticles: an active nanocatalyst for microwave irradiated solvent free synthesis of chalcones. Mater. Res. Express 7, 016116. https://doi.org/10.1088/2053-1591/ab6c9c (2020).

Article ADS CAS Google Scholar

Hölscher, J., Andersen, H. L., Saura-Múzquiz, M., Garbus, P. G. & Christensen, M. Correlation between microstructure, cation distribution and magnetism in Ni1−xZnxFe2O4 nanocrystallites. CrystEngComm 22, 515–524. https://doi.org/10.1039/C9CE01324E (2020).

Article Google Scholar

Thakur, P., Chahar, D., Taneja, S., Bhalla, N. & Thakur, A. A review on MnZn ferrites: synthesis, characterization and applications. Ceram. Int. 46, 15740–15763. https://doi.org/10.1016/j.ceramint.2020.03.287 (2020).

Article CAS PubMed PubMed Central Google Scholar

Nakamura, T., Tsutaoka, T. & Hatakeyama, K. Frequency dispersion of permeability in ferrite composite materials. J. Magn. Magn. Mater. 138, 319–328. https://doi.org/10.1016/0304-8853(94)90054-X (1994).

Article ADS CAS Google Scholar

Nakamura, T. Snoek’s limit in high-frequency permeability of polycrystalline Ni–Zn, Mg–Zn, and Ni–Zn–Cu spinel ferrites. J. Appl. Phys. 88, 348–353. https://doi.org/10.1063/1.373666 (2000).

Article ADS CAS Google Scholar

Massoudi, J. et al. Magnetic and spectroscopic properties of Ni–Zn–Al ferrite spinel: from the nanoscale to microscale. RSC Adv. 10, 34556–34580. https://doi.org/10.1039/D0RA05522K (2020).

Article ADS CAS Google Scholar

Masoudpanah, S. M., Seyyed Ebrahimi, S. A., Derakhshani, M. & Mirkazemi, S. M. Structure and magnetic properties of La substituted ZnFe2O4 nanoparticles synthesized by sol–gel autocombustion method. J. Magn. Magn. Mater. 370, 122–126. https://doi.org/10.1016/j.jmmm.2014.06.062 (2014).

Article ADS CAS Google Scholar

Ahmed, T. T., Rahman, I. Z. & Rahman, M. A. Study on the properties of the copper substituted NiZn ferrites. J. Mater. Process. Technol. 153–154, 797–803. https://doi.org/10.1016/j.jmatprotec.2004.04.188 (2004).

Article CAS Google Scholar

Naughton, B. T. & Clarke, D. R. Lattice expansion and saturation magnetization of nickel–zinc ferrite nanoparticles prepared by aqueous precipitation. J. Am. Ceram. Soc. 90, 3541–3546. https://doi.org/10.1111/j.1551-2916.2007.01980.x (2007).

Article CAS Google Scholar

Sivakumar, N., Narayanasamy, A., Ponpandian, N. & Govindaraj, G. Grain size effect on the dielectric behavior of nanostructured Ni0.5Zn0.5Fe2O4. J. Appl. Phys. 101, 084116. https://doi.org/10.1063/1.2721379 (2007).

Article ADS CAS Google Scholar

Huang, X., Zhang, J., Lai, M. & Sang, T. Preparation and microwave absorption mechanisms of the NiZn ferrite nanofibers. J. Alloys Compd. 627, 367–373. https://doi.org/10.1016/j.jallcom.2014.11.235 (2015).

Article CAS Google Scholar

Naughton, B. T., Majewski, P. & Clarke, D. R. Magnetic properties of nickel–zinc ferrite toroids prepared from nanoparticles. J. Am. Ceram. Soc. 90, 3547–3553. https://doi.org/10.1111/j.1551-2916.2007.01981.x (2007).

Article CAS Google Scholar

Song, S., Song, Q., Li, J., Mudinepalli, V. R. & Zhang, Z. Characterization of submicrometer-sized NiZn ferrite prepared by spark plasma sintering. Ceram. Int. 40, 6473–6479. https://doi.org/10.1016/j.ceramint.2013.11.099 (2014).

Article CAS Google Scholar

Sung-Soo, K., Dae-Hee, H. & Sung-Baeg, C. Microwave absorbing properties of sintered Ni–Zn ferrite. IEEE Trans. Magn. 30, 4554–4556. https://doi.org/10.1109/20.334146 (1994).

Article ADS Google Scholar

Kakirde, A., Sinha, B. & Sinha, S. N. Development and characterization of nickel–zinc spinel ferrite for microwave absorption at 2·4 GHz. Bull. Mater. Sci. 31, 767–770. https://doi.org/10.1007/s12034-008-0121-2 (2008).

Article CAS Google Scholar

Prasath, S. D. R., Balaji, S., Raju, S. & Abhaikumar, V. Synthesis and characterization of zinc substituted nickel ferrite materials for L band antenna applications. J. Mater. Sci. Mater. Electron. 27, 8247–8253. https://doi.org/10.1007/s10854-016-4831-8 (2016).

Article CAS Google Scholar

Aggarwal, N. & Narang, S. B. X-band microwave analysis and characterization of zinc substituted nickel ferrites prepared by sol–gel citrate route. J. Electron. Mater. 49, 668–680. https://doi.org/10.1007/s11664-019-07694-6 (2020).

Article ADS CAS Google Scholar

Mustaffa, M. S., Azis, R. A. S., Abdullah, N. H., Ismail, I. & Ibrahim, I. R. An investigation of microstructural, magnetic and microwave absorption properties of multi-walled carbon nanotubes/Ni0.5Zn0.5Fe2O4. Sci. Rep. 9, 15523. https://doi.org/10.1038/s41598-019-52233-2 (2019).

Article ADS CAS PubMed PubMed Central Google Scholar

Jahanbin, T., Hashim, M. & Amin Mantori, K. Comparative studies on the structure and electromagnetic properties of Ni−Zn ferrites prepared via co-precipitation and conventional ceramic processing routes. J. Magn. Magn. Mater. 322, 2684–2689. https://doi.org/10.1016/j.jmmm.2010.04.008 (2010).

Article ADS CAS Google Scholar

Hajalilou, A., Mazlan, S. A. & Shameli, K. A comparative study of different concentrations of pure Zn powder effects on synthesis, structure, magnetic and microwave-absorbing properties in mechanically-alloyed Ni–Zn ferrite. J. Phys. Chem. Solids 96–97, 49–59. https://doi.org/10.1016/j.jpcs.2016.05.001 (2016).

Article ADS CAS Google Scholar

Andhare, D. D. et al. Structural and chemical properties of ZnFe2O4 nanoparticles synthesised by chemical co-precipitation technique. J. Phys. Conf. Ser. 1644, 012014. https://doi.org/10.1088/1742-6596/1644/1/012014 (2020).

Article CAS Google Scholar

Verma, R., Mazaleyrat, F., Deshpande, U. P. & Kane, S. N. Ni addition induced modification of structural, magnetic properties and bandgap of Ni–Zn nano ferrites. Mater. Today Proc. 32, 329–333. https://doi.org/10.1016/j.matpr.2020.01.489 (2020).

Article CAS Google Scholar

Idris, F. M. et al. Broadening of EM energy-absorption frequency band by micrometer-to-nanometer grain size reduction in NiZn ferrite. IEEE Trans. Magn. 49, 5475–5479. https://doi.org/10.1109/TMAG.2013.2271219 (2013).

Article ADS CAS Google Scholar

Lakshmi, K., John, H., Mathew, K. T., Joseph, R. & George, K. E. Microwave absorption, reflection and EMI shielding of PU–PANI composite. Acta Mater. 57, 371–375. https://doi.org/10.1016/j.actamat.2008.09.018 (2009).

Article ADS CAS Google Scholar

Wang, G., Ong, S. J. H., Zhao, Y., Xu, Z. J. & Ji, G. Integrated multifunctional macrostructures for electromagnetic wave absorption and shielding. J. Mater. Chem. A 8, 24368–24387. https://doi.org/10.1039/D0TA08515D (2020).

Article CAS Google Scholar

Shimba, K., Furuta, K., Morimoto, N., Tezuka, N. & Sugimoto, S. Microwave absorption properties of polymer modified Ni–Zn ferrite nanoparticles. Mater. Trans. 52, 740–745. https://doi.org/10.2320/matertrans.MBW201013 (2011).

Article CAS Google Scholar

Yoo, J.-E. & Kang, Y.-M. Electromagnetic wave absorbing properties of Ni–Zn ferrite powder–epoxy composites in GHz range. J. Magn. Magn. Mater. 513, 167075. https://doi.org/10.1016/j.jmmm.2020.167075 (2020).

Article CAS Google Scholar

Naidu, K. C. B. & Madhuri, W. Microwave processed bulk and nano NiMg ferrites: a comparative study on X-band electromagnetic interference shielding properties. Mater. Chem. Phys. 187, 164–176. https://doi.org/10.1016/j.matchemphys.2016.11.062 (2017).

Article CAS Google Scholar

Izumi, F. In Analytical Spectroscopy Library Vol. 7 (eds Saisho, H. & Gohshi, Y.) 405–452. https://doi.org/10.1016/S0926-4345(96)80008-3(Elsevier, 1996).

Somvanshi, S. B. et al. Structural, thermal, spectral, optical and surface analysis of rare earth metal ion (Gd3+) doped mixed Zn–Mg nano-spinel ferrites. Ceram. Int. 46, 13170–13179. https://doi.org/10.1016/j.ceramint.2020.02.091 (2020).

Article CAS Google Scholar

Jalaly, M., Enayati, M. H. & Karimzadeh, F. Investigation of structural and magnetic properties of nanocrystalline Ni0.3Zn0.7Fe2O4 prepared by high energy ball milling. J. Alloys Compd. 480, 737–740. https://doi.org/10.1016/j.jallcom.2009.02.042 (2009).

Article CAS Google Scholar

Bid, S. & Pradhan, S. K. Characterization of crystalline structure of ball-milled nano-Ni–Zn-ferrite by Rietveld method. Mater. Chem. Phys. 84, 291–301. https://doi.org/10.1016/j.matchemphys.2003.08.012 (2004).

Article CAS Google Scholar

Somvanshi, S. B., Khedkar, M. V., Kharat, P. B. & Jadhav, K. M. Influential diamagnetic magnesium (Mg2+) ion substitution in nano-spinel zinc ferrite (ZnFe2O4): thermal, structural, spectral, optical and physisorption analysis. Ceram. Int. 46, 8640–8650. https://doi.org/10.1016/j.ceramint.2019.12.097 (2020).

Article CAS Google Scholar

Ehi-Eromosele, C. O., Ita, B. I., Iweala, E. E., Adalikwu, S. A. & Anawe, L. P. A. Magneto-structural properties of Ni–Zn nanoferrites synthesized by the low-temperature auto-combustion method. Bull. Mater. Scie. 38, 1465–1472. https://doi.org/10.1007/s12034-015-1038-1 (2015).

Article CAS Google Scholar

Wang, Z., Schiferl, D., Zhao, Y. & O’Neill, H. S. C. High pressure Raman spectroscopy of spinel-type ferrite ZnFe2O4. J. Phys. Chem. Solids 64, 2517–2523. https://doi.org/10.1016/j.jpcs.2003.08.005 (2003).

Article ADS CAS Google Scholar

Cynn, H., Sharma, S. K., Cooney, T. F. & Nicol, M. High-temperature Raman investigation of order–disorder behavior in the MgAl2O4 spinel. Phys. Rev. B 45, 500–502. https://doi.org/10.1103/PhysRevB.45.500 (1992).

Article ADS CAS Google Scholar

Wang, Z., Lazor, P., Saxena, S. K. & O’Neill, H. S. C. High pressure Raman spectroscopy of ferrite MgFe2O4. Mater. Res. Bull. 37, 1589–1602. https://doi.org/10.1016/S0025-5408(02)00819-X (2002).

Article CAS Google Scholar

Ma, Y. et al. Tunable microwave absorption property of magnetic nanocomposite coating by surface roughness. J. Mater. Sci. Mater. Electron. 31, 994–1003. https://doi.org/10.1007/s10854-019-02611-3 (2020).

Article CAS Google Scholar

Arboleda, J. D. et al. Evidence of the spin Seebeck effect in Ni–Zn ferrites polycrystalline slabs. Solid State Commun. 270, 140–146. https://doi.org/10.1016/j.ssc.2017.12.002 (2018).

Article ADS CAS Google Scholar

Reddy, M. P. et al. Magnetic properties of Ni–Zn ferrites prepared by microwave sintering method. J. Electroceram. 28, 1–9. https://doi.org/10.1007/s10832-011-9670-7 (2012).

Article CAS Google Scholar

Mangalaraja, R. V., Lee, S. T., Ramam, K. V. S., Ananthakumar, S. & Manohar, P. Mechanical characterization of Ni1−xZnxFe2O4 prepared by non-conventional methods. Mater. Sci. Eng. A 480, 266–270. https://doi.org/10.1016/j.msea.2007.08.021 (2008).

Article CAS Google Scholar

Aqeel, A. et al. Surface sensitivity of the spin Seebeck effect. J. Appl. Phys. 116, 153705. https://doi.org/10.1063/1.4897933 (2014).

Article ADS CAS Google Scholar

Aggarwal, N. & Narang, S. B. Magnetic characterization of nickel–zinc spinel ferrites along with their microwave characterization in Ku band. J. Magn. Magn. Mater. 513, 167052. https://doi.org/10.1016/j.jmmm.2020.167052 (2020).

Article CAS Google Scholar

Liu, Z., Peng, Z., Lv, C. & Fu, X. Doping effect of Sm3+ on magnetic and dielectric properties of Ni–Zn ferrites. Ceram. Int. 43, 1449–1454. https://doi.org/10.1016/j.ceramint.2016.10.112 (2017).

Article CAS Google Scholar

Humbe, A. V., Kounsalye, J. S., Somvanshi, S. B., Kumar, A. & Jadhav, K. M. Cation distribution, magnetic and hyperfine interaction studies of Ni–Zn spinel ferrites: role of Jahn Teller ion (Cu2+) substitution. Mater. Adv. 1, 880–890. https://doi.org/10.1039/D0MA00251H (2020).

Article CAS Google Scholar

Guire, M. R. D., O’Handley, R. C. & Kalonji, G. The cooling rate dependence of cation distributions in CoFe2O4. J. Appl. Phys. 65, 3167–3172. https://doi.org/10.1063/1.342667 (1989).

Article ADS Google Scholar

Chen, L. F., Ong, C. K., Neo, C. P., Varadan, V. V. & Varadan, V. K. In Microwave Electronics: Measurement and Materials Characterization Ch. 1, 1–36. https://doi.org/10.1002/0470020466.ch1(Wiley, 2004).

Jazirehpour, M. & Ebrahimi, S. A. S. Synthesis of magnetite nanostructures with complex morphologies and effect of these morphologies on magnetic and electromagnetic properties. Ceram. Int. 42, 16512–16520. https://doi.org/10.1016/j.ceramint.2016.07.067 (2016).

Article CAS Google Scholar

Wan, G. et al. Uniform Fe3O4 coating on flower-like ZnO nanostructures by atomic layer deposition for electromagnetic wave absorption. Dalton Trans. 44, 18804–18809. https://doi.org/10.1039/C5DT03069B (2015).

Article CAS PubMed Google Scholar

Lopes, B. H. K. et al. X band electromagnetic property influence of multi-walled carbon nanotube in hybrid MnZn ferrite and carbonyl iron composites. J. Mark. Res. 9, 2369–2375. https://doi.org/10.1016/j.jmrt.2019.12.068 (2020).

Article CAS Google Scholar

Heidari, P. & Masoudpanah, S. M. A facial synthesis of MgFe2O4/RGO nanocomposite powders as a high performance microwave absorber. J. Alloys Compd. 834, 155166. https://doi.org/10.1016/j.jallcom.2017.12.179 (2020).

Article CAS Google Scholar

Abdeen, A. M. Dielectric behaviour in Ni–Zn ferrites. J. Magn. Magn. Mater. 192, 121–129. https://doi.org/10.1016/S0304-8853(98)00324-2 (1999).

Article ADS CAS Google Scholar

Jian, X. et al. Facile synthesis of Fe3O4/GCs composites and their enhanced microwave absorption properties. ACS Appl. Mater. Interfaces 8, 6101–6109. https://doi.org/10.1021/acsami.6b00388 (2016).

Article CAS PubMed Google Scholar

Liu, P., Yao, Z., Zhou, J., Yang, Z. & Kong, L. B. Small magnetic Co-doped NiZn ferrite/graphene nanocomposites and their dual-region microwave absorption performance. J. Mater. Chem. C 4, 9738–9749. https://doi.org/10.1039/C6TC03518C (2016).

Article CAS Google Scholar

Sun, K. et al. Contribution of magnetization mechanisms in nickel–zinc ferrites with different grain sizes and its temperature relationship. Mater. Chem. Phys. 175, 131–137. https://doi.org/10.1016/j.matchemphys.2016.03.002 (2016).

Article CAS Google Scholar

Barba, A., Clausell, C., Jarque, J. C. & Nuño, L. Magnetic complex permeability (imaginary part) dependence on the microstructure of a Cu-doped Ni–Zn-polycrystalline sintered ferrite. Ceram. Int. 46, 14558–14566. https://doi.org/10.1016/j.ceramint.2020.02.255 (2020).

Article CAS Google Scholar

Song, N.-N. et al. Exceeding natural resonance frequency limit of monodisperse Fe3O4 nanoparticles via superparamagnetic relaxation. Sci. Rep. 3, 3161. https://doi.org/10.1038/srep03161 (2013).

Article PubMed PubMed Central Google Scholar

Fu, L.-S., Jiang, J.-T., Xu, C.-Y. & Zhen, L. Synthesis of hexagonal Fe microflakes with excellent microwave absorption performance. CrystEngComm 14, 6827–6832. https://doi.org/10.1039/C2CE25836F (2012).

Article CAS Google Scholar

Nakamura, T. Low-temperature sintering of NiZnCu ferrite and its permeability spectra. J. Magn. Magn. Mater. 168, 285–291. https://doi.org/10.1016/S0304-8853(96)00709-3 (1997).

Article ADS CAS Google Scholar

Li, J., Ji, H., Xu, Y., Zhang, J. & Yan, Y. Three-dimensional graphene supported Fe3O4 coated by polypyrrole toward enhanced stability and microwave absorbing properties. J. Mark. Res. 9, 762–772. https://doi.org/10.1016/j.jmrt.2019.11.016 (2020).

Article CAS Google Scholar

Caltun, O. F., Spinu, L., Stancu, A., Thung, L. D. & Zhou, W. Study of the microstructure and of the permeability spectra of Ni–Zn–Cu ferrites. J. Magn. Magn. Mater. 242–245, 160–162. https://doi.org/10.1016/S0304-8853(01)01187-8 (2002).

Article ADS Google Scholar

He, J.-Z., Wang, X.-X., Zhang, Y.-L. & Cao, M.-S. Small magnetic nanoparticles decorating reduced graphene oxides to tune the electromagnetic attenuation capacity. J. Mater. Chem. C 4, 7130–7140. https://doi.org/10.1039/C6TC02020H (2016).

Article CAS Google Scholar

Wang, H. et al. Broadband microwave absorption of CoNi@C nanocapsules enhanced by dual dielectric relaxation and multiple magnetic resonances. Appl. Phys. Lett. 102, 223113. https://doi.org/10.1063/1.4809675 (2013).

Article ADS CAS Google Scholar

Kwon, H. J., Shin, J. Y. & Oh, J. H. The microwave absorbing and resonance phenomena of Y-type hexagonal ferrite microwave absorbers. J. Appl. Phys. 75, 6109–6111. https://doi.org/10.1063/1.355476 (1994).

Article ADS CAS Google Scholar

Shin, J. Y. & Oh, J. H. The microwave absorbing phenomena of ferrite microwave absorbers. IEEE Trans. Magn. 29, 3437–3439. https://doi.org/10.1109/20.281188 (1993).

Article ADS Google Scholar

Jiao, Z. et al. Enhanced microwave absorption properties of Nd-doped NiZn ferrite/polyaniline nanocomposites. Ceram. Int. https://doi.org/10.1016/j.ceramint.2020.07.010 (2020).

Article Google Scholar

Jazirehpour, M. & Seyyed Ebrahimi, S. A. Carbothermally synthesized core–shell carbon–magnetite porous nanorods for high-performance electromagnetic wave absorption and the effect of the heterointerface. J. Alloys Compd. 639, 280–288. https://doi.org/10.1016/j.jallcom.2015.03.160 (2015).

Article CAS Google Scholar

Siva Nagasree, P., Ramji, K., Subramanyam, C., Krushnamurthy, K. & Haritha, T. Synthesis of Ni0.5Zn0.5Fe2O4-reinforced E-glass/epoxy nanocomposites for radar-absorbing structures. Plast. Rubber Compos. 49, 434–442. https://doi.org/10.1080/14658011.2020.1793080 (2020).

Article CAS Google Scholar

Aggarwal, N. & Narang, S. B. Effect of co-substitution of Co–Zr on electromagnetic properties of Ni–Zn spinel ferrites at microwave frequencies. J. Alloys Compd. https://doi.org/10.1016/j.jallcom.2020.157461 (2020).

Article Google Scholar

Ali, N. N. et al. Lightweight broadband microwave absorbers of core–shell (polypyrrole/NiZn ferrite) nanocomposites in the X-band: insights on interfacial polarization. J. Mater. Sci. Mater. Electron. 30, 6876–6887. https://doi.org/10.1007/s10854-019-01002-y (2019).

Article CAS Google Scholar

Han, Q., Meng, X. & Lu, C. Exchange-coupled Ni0.5Zn0.5Fe2O4/SrFe12O19 composites with enhanced microwave absorption performance. J. Alloys Compd. 768, 742–749. https://doi.org/10.1016/j.jallcom.2018.07.310 (2018).

Article CAS Google Scholar

Flaifel, M. H. et al. Preparation, thermal, magnetic and microwave absorption properties of thermoplastic natural rubber matrix impregnated with NiZn ferrite nanoparticles. Compos. Sci. Technol. 96, 103–108. https://doi.org/10.1016/j.compscitech.2014.03.016 (2014).

Article CAS Google Scholar

Li, X. et al. Fabrication of three-dimensional flower-like heterogeneous Fe3O4/Fe particles with tunable chemical composition and microwave absorption performance. ACS Appl. Mater. Interfaces 11, 19267–19276. https://doi.org/10.1021/acsami.9b01783 (2019).

Article CAS PubMed Google Scholar

Yan, F. et al. Growth of CoFe2O4 hollow nanoparticles on graphene sheets for high-performance electromagnetic wave absorbers. J. Mater. Chem. C 6, 12781–12787. https://doi.org/10.1039/C8TC04222E (2018).

Article CAS Google Scholar

Li, D., Zhang, B., Liu, W., Liang, X. & Ji, G. Tailoring the input impedance of FeCo/C composites with efficient broadband absorption. Dalton Trans. 46, 14926–14933. https://doi.org/10.1039/C7DT02840G (2017).

Article CAS PubMed Google Scholar

Download references

Department of Materials Engineering, Tarbiat Modares University, 14115-143, Tehran, Iran

M. Derakhshani & E. Taheri-Nassaj

Department of Electroceramics and Electrical Engineering, Malek Ashtar University of Technology, Tehran, Iran

M. Jazirehpour

School of Metallurgy and Materials Engineering, Iran University of Science and Technology (IUST), Narmak, Tehran, Iran

S. M. Masoudpanah

You can also search for this author in PubMed Google Scholar

You can also search for this author in PubMed Google Scholar

You can also search for this author in PubMed Google Scholar

You can also search for this author in PubMed Google Scholar

All authors have contributed to the present research. M.D.: Synthesis, Characterization, Conceptualization, Writing the manuscript text and preparing figures. E.T.-N.: Supervision, Review and editing the main manuscript, Conceptualization. M.J.: Supervision, Characterization. S.M.M.: Supervision, Conceptualization, Reviewing and editing the manuscript text and figures. All authors approved the final manuscript.

Correspondence to E. Taheri-Nassaj.

The authors declare no competing interests.

Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made. The images or other third party material in this article are included in the article's Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article's Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this licence, visit http://creativecommons.org/licenses/by/4.0/.

Reprints and permissions

Derakhshani, M., Taheri-Nassaj, E., Jazirehpour, M. et al. Structural, magnetic, and gigahertz-range electromagnetic wave absorption properties of bulk Ni–Zn ferrite. Sci Rep 11, 9468 (2021). https://doi.org/10.1038/s41598-021-88930-0

Download citation

Received: 04 February 2021

Accepted: 19 April 2021

Published: 04 May 2021

DOI: https://doi.org/10.1038/s41598-021-88930-0

Anyone you share the following link with will be able to read this content:

Sorry, a shareable link is not currently available for this article.

Provided by the Springer Nature SharedIt content-sharing initiative

Scientific Reports (2024)

Indian Journal of Physics (2024)

Journal of Electronic Materials (2023)

Journal of Materials Science (2022)

Plasmonics (2022)